TACKWHITE A 83 is a low Tg pure Acrylic polymer emulsion that forms extremly clear, elastic and tacky films when dried over 0°C . The dried film has a very aggressive initial tack and a good cohesion.
TACKWHITE A 83 is suitable for the production of pressure sensitive packaging and office tapes on BOPP films. By applying approximately 20-21 g/sqm dry weight, it yields a good balance of peel and shear strength. It is supplied as a ready-to-use emulsion and it is suitable for most of today's modern coating machines. With TACKWHITE A 83 it is possible to produce BOPP tapes with low unwinding noise, by corona treating the backside of the film.
Other prerogatives:
- Very aggressive initial tack
- Good adhesivity
- Good properties with low amounts/sqm
Method of analysis | MU | Standard | |
---|---|---|---|
1 | Total Solids | % | 53±0.50 |
8 | pH | pH | 9 - 10 |
Solvents | water | ||
3 | Brookfield Viscosity 25°C | mPa.s | |
• | TACKWHITE A 83 | 200 - 6001 | |
• | TACKWHITE A 83 (V) | 800 - 9001 | |
Notes | |||
1 | N. 2 RV; 20 RPM |
Method of analysis | MU | Standard | |
---|---|---|---|
11 | Peel Adhesion on Steel | g/in | 600 - 900 |
22 | Static Shear | h | > 50 |
97 | Loop Tack Test | g | 950 |
Average values; 22±2 g/m² of dry adhesive on PET film 36 µm |
The product is supplied in iron drums (200 kg); IBC containers (1000 kg).
To ensure safe storage of this emulsion, containers should be well sealed to prevent water evaporation and skin formation. The emulsion must be stored at 5-40°C.
Use within 6 months from production date (unopened and in the original packaging).
Mod. DT3002E | Creation date: 7/26/2004 | Revision: 6 | Revision date: 26 Aug 2021 |