Description
TACKSOL NIS 6 is a solvent pressure sensitive adhesive, based on different rubbers and special resins, with very high peel adhesion.
Application
TACKSOL NIS 6 can be applied on any substrate (textile, TNT, paper, polyester, PP, PE, PVC). It is suggested when high adhesivity, high tack and good cohesion are required.
Technical Specifications
| Method of analysis | MU | Standard | |
|---|---|---|---|
| 1 | Total Solids | % | 48±1 |
| 3 | Brookfield Viscosity 25°C | mPa.s | 30,000 - 45,0001 |
| Solvents | toluene | ||
| Notes | |||
| 1 | No 6 RV; 10 RPM | ||
Film properties
| Method of analysis | MU | Standard | |
|---|---|---|---|
| 11 | Peel Adhesion on Steel | g/in | 2,000 |
| 96 | S.A.F.T.1 | °C | 120 |
| 97 | Loop Tack Test | g | 3,000 |
| Notes | |||
| 1 | based on ASTM D4498-00 | ||
| Average values; 22±2 g/m² of dry adhesive on PET film 36 µm | |||
Handling
TACKSOL NIS 6 can be coated with rotating knife or knife-on-roll.
When heat or mechanical resistance must be increased, CURING AGENT D should be added. In this case the pot-life of the adhesive is reduced as crosslinking starts immediately after the addition of the curing agent. The amount of isocyanate depends on the final properties requested.
Packaging
The product is supplied in iron drums (145 kg).
Storing
Product must be stored in a ventilated and dry place. Avoid flames presence.
Use within 12 months from production date (unopened and in the original packaging).
| Mod. DT3002E | Creation date: 12/10/2018 | Revision: 2 | Revision date: 4 Feb 2020 |
Above information is reliable, but does not constitute warranty.