TACKWHITE A 205 SL1 is a water borne p.s.a., based on natural and synthetic latices, properly stabilised and thickened.
TACKWHITE A 205 SL1 has excellent ageing properties and permits to obtain very stable p.s.a. It contains the best available antioxidants, however, being based on SBR latices, it yelds transparent but slightly yellowish films.
The product does not contain organic solvents.
Permanent paper labels; fabrics; synthetic leathers; polyurethane, PE, PVC foams; paper and paperboards; etc., with very high peel adhesion and good resistance to elevated temperatures (until 70°C).
Method of analysis | MU | Standard | |
---|---|---|---|
1 | Total Solids | % | 52±2 |
8 | pH | pH | 8 - 9 |
Solvents | water | ||
3 | Brookfield Viscosity 25°C | mPa.s | |
• | TACKWHITE A 205 SL1 (V1) | 12000 - 170001 | |
• | TACKWHITE A 205 SL1 (V2) | 17000 - 270002 | |
Notes | |||
1 | N. 5 RV; 20 RPM | ||
2 | No 6 RV; 20 RPM |
Method of analysis | MU | Standard | |
---|---|---|---|
11 | Peel Adhesion on Steel | g/in | 1,000 |
22 | Static Shear | h | > 5 |
96 | S.A.F.T.1 | °C | > 80 |
97 | Loop Tack Test | g | 1,600 |
Notes | |||
1 | based on ASTM D4498-00 | ||
Average values; 22±2 g/m² of dry adhesive on PET film 36 µm |
When a higher cohesion is required, we suggest to add 0.2% - 0.4% of CURING AGENT W3 or CURING AGENT X7.
The product is supplied in iron drums (200 kg); IBC containers (1000 kg).
TACKWHITE A 205 SL1 must be stored at temperatures between +5 and +40°C .
Use within 6 months from production date (unopened and in the original packaging).
Mod. DT3002E | Creation date: 2/17/2017 | Revision: 3 | Revision date: 8 Jul 2019 |