Description
SOLACRIL 306 is a solvent borne acrylic PSA, with a very good resistance to ageing, light and heat.
Application
SOLACRIL 306 can be applied on various substrates: paper, polyester, PP, PE, PVC, etc. It has a very good wettability on various substrates, especially on rough surfaces.
After curing it is recommended for protective films.
Technical Specifications
| Method of analysis | MU | Standard | |
|---|---|---|---|
| Solvents | ethylacetate | ||
| 1 | Total Solids | % | |
| • | SOLACRIL 306 | 52.5±1 | |
| 3 | Brookfield Viscosity 25°C | mPa.s | |
| • | SOLACRIL 306 | 2,000 - 6,0001 | |
| Notes | |||
| 1 | N. 4 RV; 20 RPM | ||
Film properties
| 11 | Peel Adhesion on Steel | g/in | |
| • | SOLACRIL 306 | 2401 | |
| 97 | Loop Tack Test | g | |
| • | SOLACRIL 306 | 5401 | |
| Notes | |||
| 1 | Crosslinked with 0.2% of CURING AGENT CH | ||
| Average values; pilot plant coating at 1 m/min; 18±3 g/m² on PET film 23 µm, TCA-treated | |||
Handling
SOLACRIL 306 must be activated before its use, to increase adhesion to plastic films and to improve cohesion.
Suggested activators are: CURING AGENT CH, CURING AGENT D or RF/AEDE. Reaction starts immediately, so it is recommended to use the product after activation. The quantity of crosslinker depends on the coating weight and on the desired final properties, usually it is between 0.2 and 1.5%. We suggest to check in advance the curing conditions.
Storing
Store in a cool place, protected from direct sunlight and heat sources, at temperatures between +5 and +40°C. Keep material in tightly closed containers to prevent loss of solvent.
| Mod. DT3002E | Creation date: 7/15/2016 | Revision: 1 | Revision date: 15 Jul 2016 |
Above information is reliable, but does not constitute warranty.
ICHEMCO srl
via 11 Settembre, 5 - 20012 CUGGIONO (MI) - ITALY
Phone: +39 02 97243.1 - Fax: +39 02 97243.200
- internet: www.ichemco.it
via 11 Settembre, 5 - 20012 CUGGIONO (MI) - ITALY
Phone: +39 02 97243.1 - Fax: +39 02 97243.200
- internet: www.ichemco.it