SOLACRIL 206 is a solvent borne acrylic PSA, with a very good resistance to ageing, light and heat.
SOLACRIL 206 can be applied on various substrates: paper, polyester, PP, PE, PVC, etc. It has a very good wettability on various substrates.
After curing it is recommended for protective films.
Method of analysis | MU | Standard | |
---|---|---|---|
Solvents | ethylacetate | ||
1 | Total Solids | % | |
• | SOLACRIL 206 | 43±1 | |
3 | Brookfield Viscosity 25°C | mPa.s | |
• | SOLACRIL 206 | 1,000 - 3,0001 | |
Notes | |||
1 | No 3 RV; 20 RPM |
11 | Peel Adhesion on Steel | g/in | |
• | SOLACRIL 206 | 701 | |
97 | Loop Tack Test | g | |
• | SOLACRIL 206 | 2001 | |
Notes | |||
1 | Crosslinked with 0.2% of CURING AGENT CH | ||
Average values; pilot plant coating at 1 m/min; 18±3 g/m² on PET film 23 µm, TCA-treated |
SOLACRIL 206 must be activated before its use, to increase adhesion to plastic films and to improve cohesion.
Suggested activators are: CURING AGENT CH, CURING AGENT D or RF/AEDE. Reaction starts immediately, so it is recommended to use the product immediately after activation. The quantity of crosslinker depends on the coating weight and on the desired final properties, usually it is between 0.2 and 1.5%. We suggest to check in advance the curing conditions.
The product is supplied in iron drums (180 kg).
Store in a cool place, protected from direct sunlight and heat sources, at temperatures between +5 and +40°C. Keep material in tightly sealed containers to prevent loss of solvent.