Description
SOLACRIL 758 B is a self cross-linking modified acrylic pressure sensitive adhesive. The product does not contain aromatic solvents.
SOLACRIL 758 B has high tack and peel adhesion values.
Application
SOLACRIL 758 B is suitable for application on low surface tension substrates.
Technical Specifications
| Method of analysis | MU | Standard | |
|---|---|---|---|
| 1 | Total Solids | % | 53±1 |
| 3 | Brookfield Viscosity 25°C | mPa.s | 2,000 - 5,0001 |
| Solvents | ethylacetate / isopropyl alcohol | ||
| Notes | |||
| 1 | No 3 RV; 20 RPM | ||
Film properties
| Method of analysis | MU | Standard | |
|---|---|---|---|
| 11 | Peel Adhesion on Steel | g/in | 1,700 |
| 22 | Static Shear | h | > 100 |
| 96 | S.A.F.T.1 | °C | 144 |
| 97 | Loop Tack Test | g | 2,000 |
| Notes | |||
| 1 | based on ASTM D4498-00 | ||
| Average values; pilot plant coating at 1 m/min; 25±3 g/m² on PET film 23 µm, TCA-treated | |||
Handling
SOLACRIL 758 B is supplied ready for coating by rotating blade or reverse roll. Diluted, it can be applied by rotogravure or Mayer bar. A perfect drying is necessary to fully complete the cross-linking process: residual solvent might prevent a good cross-linking, impacting on the final quality of the product. We don’t recommend further addition of crosslinker.
Packaging
The product is supplied in iron drums (180 kg); ADR compliant IBC containers (900 kg).
Storing
Store in a cool place, protected from direct sunlight and heat sources, at temperatures between +5 and +40°C. Keep material in tightly closed containers to prevent loss of solvents.
Use within 6 months from production date (unopened and in the original packaging).
| Mod. DT3002E | Creation date: 10/19/2012 | Revision: 8 | Revision date: 24 Jul 2018 |
Above information is reliable, but does not constitute warranty.