TACKWHITE A 305 SL is a water borne pressure sensitive adhesive, based on anionic dispersion of carboxilated SBR latex modified with tackifiers.
TACKWHITE A 305 SL allows to obtain pressure sensitive adhesives with very high peel adhesion .
Foams, fabrics, synthetic leathers, paper boards, with high adhesive power.
Method of analysis | MU | Standard | |
---|---|---|---|
1 | Total Solids | % | 50±1 |
8 | pH | pH | 8 - 9 |
Solvents | water | ||
3 | Brookfield Viscosity 25°C | mPa.s | |
• | TACKWHITE A 305 SL | < 2501 | |
• | TACKWHITE A 305 SL (V2) | 17,000 - 27,0002 | |
• | TACKWHITE A 305 SL (V3) | 27,000 - 37,0002 | |
Notes | |||
1 | No 1 RV; 100 RPM | ||
2 | No 6 RV; 20 RPM |
Method of analysis | MU | Standard | |
---|---|---|---|
11 | Peel Adhesion on Steel | g/in | 1,800 |
22 | Static Shear | h | > 15 |
97 | Loop Tack Test | g | 1,300 |
Average values; 22±2 g/m² of dry adhesive on PET film 36 µm |
Cohesion can be increased by adding a small amount (0.2 - 0.4%) of CURING AGENT W3 or CURING AGENT X7.
The product is supplied in iron drums (200 kg); IBC containers (1000 kg).
TACKWHITE A 305 SL must be stored at temperatures between +5 and +40°C.
Use within 6 months from production date (unopened and in the original packaging).
Formulations based on synthetic latices, once coated, may be subject to a physiological decline of the adhesive performance.